Comparative study between conventional and microwave sintered lead-free BNKT ceramics
Chen P.-Y.2; Chou C.-C.2; Tseng T.-Y.4; Chen H.H.D.3
2009-12-01
Conference Name6th Asian Meeting on Ferroelectrics
Source PublicationFerroelectrics
Volume381
Issue1 PART 2
Pages196-200
Conference DateAUG 02-06, 2008
Conference PlaceTaipei, TAIWAN
Abstract

Lead free [(1-x)Bi0.5Na0.5TiO3-(x)Bi0.5K0.5TiO3] ceramics with x = 0.18 were prepared by using microwave sintering technique. XRD of these ceramics show co-existence of tetragonal and rhombohedral phases. Smaller grain size and more uniform microstructure were observed in microwave sintered sample. It might result from different diffusion mechanism. The activation energy of grain growth was calculated. The results display in microwave sintered sample is lower (167kJ/mol) than that for conventional one (260kJ/mol). It implies microwave sintered sample just need lower energy for densification. The remanent polarization and piezoelectric constants of microwave sintered samples are higher than that of conventional sintered samples. Relation among processing kinetics, microstructural characteristics and electrical properties was discussed. Copyright © Taylor & Francis Group, LLC.

KeywordFerroelectric Lead-free Microwave Sintering Piezoelectric
DOI10.1080/00150190902877528
URLView the original
Language英語English
WOS IDWOS:000269689400027
Scopus ID2-s2.0-77949310960
Fulltext Access
Citation statistics
Document TypeConference paper
CollectionUniversity of Macau
Affiliation1.Mingchi Institute of Technology
2.National Taiwan University of Science and Technology
3.Tunghai University
4.National Taipei University of Technology
Recommended Citation
GB/T 7714		 Chen P.-Y.,Chou C.-C.,Tseng T.-Y.,et al. Comparative study between conventional and microwave sintered lead-free BNKT ceramics[C], 2009, 196-200.
APA Chen P.-Y.., Chou C.-C.., Tseng T.-Y.., & Chen H.H.D. (2009). Comparative study between conventional and microwave sintered lead-free BNKT ceramics. Ferroelectrics, 381(1 PART 2), 196-200.
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[Chen P.-Y.]'s Articles
[Chou C.-C.]'s Articles
[Tseng T.-Y.]'s Articles
Baidu academic
Similar articles in Baidu academic
[Chen P.-Y.]'s Articles
[Chou C.-C.]'s Articles
[Tseng T.-Y.]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[Chen P.-Y.]'s Articles
[Chou C.-C.]'s Articles
[Tseng T.-Y.]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.