Ytterbium-doped Sr (PO ) F transparent ceramics have been developed through spark plasma sintering (SPS) with a low sintering temperature and short dwelling time. The XRD patterns show a polycrystalline hexagonal phase, and the TEM microstructure characterization indicates that the ceramics have a narrow grain size distribution which ranges from 40 to 200 nm, with an average grain size around 150 nm. The transmittance of a 2 mm thick ceramic sample is measured to be 74% at 1000 nm by a UV-Vis-NIR spectrophotometer. Furthermore, there is a strong emission peak around 1040 nm which has a lifetime of 1.06 ms and is exhibited by a PL spectrometer with the 980 nm laser diode excitation. © 2013 The American Ceramic Society.