Influences of a new admixture MX on concrete durability

Residential College	false
Status	已發表Published
	Influences of a new admixture MX on concrete durability
	Ma B.; Dong R.; Zhu H.; Zhang L.; Zhong K.; He X.; Li Z.
	2005-03-01
Source Publication	Journal Wuhan University of Technology, Materials Science Edition
ISSN	10002413
Volume	20 Issue:1 Pages:117-120
Abstract	The performance of concrete with a new admixture MX was studied by using the freeze-thaw cycle, permeability and chemical attack test. The experimental results show that MX improves the durability of concrete. Within the optimum proportion ranges from 0.1% to 1%, the compressive strength of concrete after freeze-thaw is increased by 20%-50%, and Young's modulus can be increased by 3.76-5.64 times. The strength and weight loss of concrete with 0.4% MX are respectively decreased by 28% and 60% after hydrochloric acid attack. The strength and weight loss of concrete with 0.4% MX are decreased by 5%-20% after sulfuric acid and sodium sulfate attack. The permeability of concrete with 1% MX at 28 days can be decreased by more than 30%. The investigation of the negative temperature property of MX and analysis on concrete composition and microstructure by MIP reveal that the heat conduction is resisted and the freezing procedure of solution in concrete pore is retarded due to the adding of MX. Moreover, the pore structure of concrete with MX is improved, thus improving the durability. Based on this study, a resistance model of MX to block the heat and mass transference was proposed, and the mechanism of durability improvement of concrete with MX was explained.
Keyword	MX durability admixture Negative temperature property Ratio of strength loss
URL	View the original
Language	英語English
Fulltext Access	View Full-Text via Scopus
Document Type	Journal article
Collection	University of Macau
Affiliation	Wuhan University of Technology
Recommended Citation GB/T 7714	Ma B.,Dong R.,Zhu H.,et al. Influences of a new admixture MX on concrete durability[J]. Journal Wuhan University of Technology, Materials Science Edition, 2005, 20(1), 117-120.
APA	Ma B.., Dong R.., Zhu H.., Zhang L.., Zhong K.., He X.., & Li Z. (2005). Influences of a new admixture MX on concrete durability. Journal Wuhan University of Technology, Materials Science Edition, 20(1), 117-120.
MLA	Ma B.,et al."Influences of a new admixture MX on concrete durability".Journal Wuhan University of Technology, Materials Science Edition 20.1(2005):117-120.

Files in This Item:
There are no files associated with this item.

If you have any objections to this item, please fill out the form below and the administrator will contact you as soon as possible.
Content:
Email：	*
Affiliation No.
Verification Code:	Refresh

Any comments and suggestions are welcomed.
Title:	*
Content:
Email：	*
Verification Code:	Refresh